Polyamide yarns of technical purpose
POLYAMIDE YARNS OF TECHNICAL PURPOSE

93,5 tex caprone; 187 tex of technical purpose; 93,5 tex (PА-6,6) complex; 93,5 tex (PА-6,6) for fabric TSI; 29,0 tex (PА-6,6) of technical purpose; 93,5 tex х2х4; 93,5 tex х2х3х3 and 112 tex х2х3х3 - for cone belts; 93,5 tex (PА-6,6) for filtered fabrics.


Polyamide yarns of technical purpose are meant for production of rubber-technical, rope articles, for production of filtered fabrics, sewing yarns and also for production of sports fabrics.

Physico-mechanical indexes to polyamide technical yarn (PА-6) 93,5 tex; 187 tex (TU U 6-00204048.119-98 ch. 1)
Index name 187 tex 93,5 tex
Highest
quality
1 st
quality
Highest
quality
1 st
quality
1. Specific tearing force, mN/tex, not less 667,0 637,0 667,0 637,0
2. Coefficient of variation at tearing force, %, not more 6,0 7,0 6,0 7,0
3. Yarn lengthening at break, % 15,0 2,0 not more 18,7 15,0 2,0 not more 18,7
4. Coefficient of variation at lengthening, %, not more 10,0 12,0 10,0 12,0
5. Twists number per 1 m of yarn 30(+15;-10) 30(+15;-10) 30(+15;-10) 30(+15;-10)
6. Deviation of conditioned linear density from nominal one, % 3,0 5,0 3,0 5,0
7. Linear shrinkage, % 7,0 1,0 7,5 1,5 7,0 1,0 7,5 1,5
8. Mass share of spin finish, %, not more 1,2 1,2 1,2 1,2
9. Yarn mass on packing PTSG-300, kg 2,3 0,2 2,3 0,2 2,3 0,2 2,3 0,2
10. Normalised humidity of yarn, % 5,0 5,0 5,0 5,0
11. Actual of humidity of yarn, %, not more 7,0 7,0 7,0 7,0
12. Monofilaments number in complex yarn 280 280 140 140
13. Polyamide yarn is produced with the application of spin-finish FILAPAN TC-26 made in Germany
Physico-mechanical indexes to polyamide (PА-6,6) technical yarns (TU U 6-00204048.118-97; TU U 6-00204048.132-99;
TU U 6-00204048.115-97; TU U 6-00204048.059-94; TU U 6-00204048.084-96)
Index name Norm for the yarn of linear density
93,5 tex 93,5 tex х1х2 29 tex 93,5 tex х1
TSI
For cone belts 25 tex
28 tex V/P for weft
93,5 tex х2х4 93,5 tex х2х3х3 112 tex х2х3х3
Highest quality 1 st quality
1 st quality 1 st quality



1. Yarn diameter, mm




1,5+0,4
-0,2
2,1±0,3 2,1±0,3
2. Yarn tearing force, N, not less 69 66 78 14,7 54 412 981 1118 0,167
3. Coefficient of variation at tearing force, %, not more 4,0 6,0






4. Yarn lengthening at break, %, not more 15,0 16,3 23 20 20


70
5. Yarn lengthening at force 98,1 N, %, not more




6,6 3,0 3,0
6. Yarn lengthening at force 196,2 N, %, not more




9,0 6,5 6,6
7. Coefficient of variation at yarn lengthening at fracture, %, not more 8,8 10,0






8. Deviation of conditioned linear density from nominal one, % ±3,0 ±4,0 ±15 ±8 +1,5; -5 ±5,0 ±5,0 ±5,0 ±3,0
9. Twists number per 1 m of yarn
-second twisting
-third twisting
25±10


25±10


210±30
160±30

30 +15
-10

200
+40
-15

135±10
85±10


80±10

120±10
80±10
200


10. Linear shrinkage, % 6,0±0,5 6,0±1,0
not 9
not 6,5 not 6,5 not 6,6
11. Mass share of spin-finish, % 0,3 1,2 0,3 1,2
not 1,5




12. Twist direction Z Z ZS Z S SZ ZSZ ZSZ
13. Yarn mass on packing, kg, (PTSG-300; 355) 2,3±0,2 2,3±0,2 2,0±0,3 not 1,0 not 1,0 not 1,2 not 1,2 not 1,2 not 0,8
14. Monofilaments number 140 140 280 80 140 1120 2520 2520 20
15. Normalised humidity, % 5,0 5,0 5,0 5,0 5,0 5,0 5,0 5,0 5,0
16. Actual humidity, %, not more 7,0 7,0 7,0 7,0 7,0 7,0 7,0 7,0 7,0
17. Polyamide (PА-6,6) yarns are produced with the application of spin-finish FILAPAN TC-26 made in Germany
18. Polyamide (PА-6,6) yarns for weft are produced by means of combining two complex yarns 9 tex, one of which is a core yarn and the other is auxiliraly.