	NEW ASSORTMENTS The enterprise has got modern equipment, construction departments and chemical laboratories, developed services of supplying and multi thousand working staff. All these factors help to reconstruct technological process of the enterprise, to extend the assortment of produced goods. Below you can get acquainted with new assortments of our enterprise.


	Polyamide yarns of technical use	93,5 tex caprone on the cartridges PTSG - dyed (black); 187 tex of technical use on cartridges PTSG - dyed (black); 23,5 tex (PA-6,6)
	Monofilaments	Fishing 0,1-0,5 mm transparent and dyed; polyprophylene 0,15-0,70 mm transparent and dyed; they are meant for production of articles of technical use and consumer goods; polyethelene with diameter 0,2-0,25 mm transparent and dyed, wide color range.
	Caprone cord fabrics	6 KNTS-0, 123 КNTS, 30 КNTS, 302 КNTS
	Textile and technical polyamide yarns	Polyamide yarn 12,5 tex 300 tw/m; polyamide yarn 6,7 tex 130 tw/m; polyamide yarn elastic 7,75 tex (grey, blue, brown, black, not dyed)
	Polyamide yarns for fishing	15,6 tex х1х3; 29,0 tex х1х2; 93,5 tex х1х2 black; 93,5 tex х1х3; 187 tex х1х2 black; 187 tex х1х3
	Consumer goods	Technical yarn elastic warp 3,3 tex х2; technical yarn for rubber-technical articles; child's sports costumes, jempers, knickers, women's tights and others.
	Fiber for textile industry	1,7 tex

Physico-Mechanical (actual) indexes of polyethelene monofilaments (fish-line)
№	Index name	Standard for monofilaments of nominal diameter, mm
№	Index name	0,20	0,25
1.	Deviation of actual diameter from nominal one, mm	0,00	0,00
2.	Tearing force, N, not less	22,3	33,87
3.	Coefficient of variation of tearing force, %, not more	1,3	1,7
4.	Monofilament lengthening at break, %	17,7	16,5
5.	Coefficient of variation at lengthening at break, %, not more	4,0	3,85
6.	Linear shrinkage, %, not more	4,9	4,2
7.	Hardness in knot, daN	1,10	1,74
8.	Mass share of spin finish, %, not more	0,51,2	0,51,2
9.	Monofilament mass on packing, kg	1,0±0,1	1,0±0,1

Actual physico-mechanical indexes to polyprophylene monofilaments
№	Index name	Norm for monofilament of nominal diameter, mm
№	Index name	0,15	0,18	0,20	0,28	0,30
1.	Linear density, tex	21,47	32,30	36,14	85,88	80,51
2.	Deviation of actual diameter from nominal one, mm	-0,004	-0,001		+0,03
3.	Tearing force, N	14,0	15,9	20,57	39,44	47,28
4.	Monofilament lengthening at break, %	15,45	14,37	15,34	15,53	15,28
5.	Coefficient of variation at tearing force, %	2,5	6,7	5,0	2,2	4,2
6.	Coefficient of variation at lengthening at break, %	4,4	7,9	6,6	4,2	4,4
7.	Linear shrinkage, %	9,2	8,5	11,4	11,5	9,0
8.	Transparance (in marks)		6,9	7,0		7,0
9.	Monofilament mass on packing, kg	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1

Physico-mechanical (actual) indexes to polyamide (PA-6) monofilaments (fish-line) for fishing
№	Index name	Norm for monofilament of nominal diameter, mm
№	Index name	0,10	0,12	0,15	0,18	0,20	0,24	0,27	0,30	0,34	0,40	0,45	0,50
1.	Deviation of actual diameter from nominal one, mm	0,00	+0,02	0,00	-0,01	0,00	+0,01	0,00	0,00	0,00	0,00	0,00	0,00
2.	Tearing force, N, kgf, not less	8,3 0,8	12,0 1,2	17,8 1,8	25,0 2,5	29,3 2,99	45,0 4,6	53,5 5,45	61,6 6,3	73,7 7,5	100,6 10,3	137,3 14,0	140,7 14,3
3.	Coefficient of variation at tearing force, %, not more	2,5	1,8	3,7	2,3	2,6	3,1	2,1	2,4	2,2	3,1	2,0	1,5
4.	Yarn lengthening at break, %	17,3	20,0	18,1	17,1	19,4	20,3	17,9	17,8	18,1	17,1	18,1	23,7
5.	Coefficient of variation at lengthening at break, %, not more	8,2	4,2	8,9	7,7	8,2	9,8	6,0	10,0	9,6	6,9	7,8	5,8
6.	Linear shrinkage, %, not more	9,4	11,5	10,2	12,9	14,3	13,5	14,3	16,0	16,0	14,5	14,2	12,3
7.	Hardness in knot, daN	0,44	0,76	1,20	1,53	2,07	2,94	3,64	3,81	4,34	5,55	7,04	8,83
8.	Mass share of spin finish, %, not more	0,51,2	0,51,2	0,51,2	0,51,2	0,6	0,4	0,4	0,1	0,6
9.	Monofilament mass on packing, kg	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1	1,0±0,1
Note: there is a possibility to produce colored monofilaments.